Nickel‒cobalt bimetallic catalysts prepared from hydrotalcite-like compounds for dry reforming of methane

Ni–Co/Mg(Al)O alloy catalysts with different Co/Ni molar ratios have been prepared from Ni- and Co-substituted Mg–Al hydrotalcite-like compounds (HTlcs) as precursors and tested for dry reforming of methane. The XRD characterization shows that Ni–Co–Mg–Al HTlcs are decomposed by calcination into Mg(Ni,Co,Al)O solid solution, and by reduction finely dispersed alloy particles are formed. H₂-TPR indicates a strong interaction between nickel/cobalt oxides and magnesia, and the presence of cobalt in Mg(Ni,Co,Al)O enhances the metal-support interaction. STEM-EDX analysis reveals that nickel and cobalt cations are homogeneously distributed in the HTlcs precursor and in the derived solid solution, and by reduction the resulting Ni–Co alloy particles are composition-uniform. The Ni–Co/Mg(Al)O alloy catalysts exhibit relatively high activity and stability at severe conditions, i.e., a medium temperature of 600 °C and a high space velocity of 120000 mL g^?1 h^?1. In comparison to monometallic Ni catalyst, Ni–Co alloying effectively inhibits methane decomposition and coke deposition, leading to a marked enhancement of catalytic stability. From CO₂-TPD and TPSR, it is suggested that alloying Ni with Co favors the CO₂ adsorption/activation and promotes the elimination of carbon species, thus improving the coke resistance. Furthermore, a high and stable activity with low coking is demonstrated at 750 °C. The hydrotalcite-derived Ni–Co/Mg(Al)O catalysts show better catalytic performance than many of the reported Ni–Co catalysts, which can be attributed to the formation of Ni–Co alloy with uniform composition, proper size, and strong metal-support interaction as well as the presence of basic Mg(Al)O as support.     

Deacetylated Cellulose Acetate/Polyurethane Composite Nanofiber Membranes with Highly Efficient Oil/Water Separation and Excellent Mechanical Properties

Nowadays, oil pollution has become more serious, which causes great threats both to the ecological environment and human life. In this study, a novel type of multifunctional deacetylated cellulose acetate/polyurethane (d-M_CA:M_TPU) composite nanofiber membranes for oil/water separation are successfully fabricated by electrospinning, which show super-amphiphilicity in air, super-hydrophilicity in oil, and oleophobicity in water. All the d-M_CA:M_TPU composite nanofiber membranes with different mass ratios can be used as water-removing, oil-removing, and emulsion separation substance only by gravity driving force. The highest separation flux for water and oil reaches up to 37 000 and 74 000 L m⁻² h⁻¹, respectively, and all the separation efficiencies are more than 99%. They have outstanding comprehensive mechanics performance, which can be controlled by simply adjusting the mass ratios. They show excellent antifouling and self-cleaning ability, endowing powerful cyclic stability and reusability. Those results show that d-M_CA:M_TPU composite nanofiber membranes have great application prospects in oil/water separation.     

Finite element optimization of sample geometry for measuring the torsional shear strength of glass/metal joints

Assessment of mechanical properties of glass/metal joints is a challenging process, especially when the application relevant conditions of the joints have to be considered in the test design. In this study, a finite element method (FEM) is implemented to analyze a torsional shear strength test designed for glass-ceramic/steel joints aiming towards solid oxide fuel/electrolysis cells application. Deviations from axial symmetry of the square flanges (ends) of respective hourglass-shaped specimens and also supporting and loading sockets of the test set-up are included in the model to simulate conditions close to reality. Undesirable tensile stress and also shear stress concentration appear at the outer edge of glass-ceramic layers, which are less for the hollow-full specimen. The simulation results show that for a specimen with either 9 mm thick square- or 6 mm thick triangular-flanges, locally enhanced tensile stresses almost disappear, resulting in a symmetric shear stress distribution. The difference between the analytically derived nominal shear strength and the real critical shear stress derived via simulation reduces with decreasing the fracture torque.     

长走向平行钒铁矿体协同开采方案研究

七角井矿区的钒、铁双层矿体走向长度超4 km且呈近似平行产出，下盘铁矿开采时损失贫化率高且上盘钒矿资源保护难度大。根据钒铁矿体走向长、近平行产出、厚度负相关、空区隐患大的开采技术条件 特征，采用平面分区、开采时序规划、采矿方法优化、区域稳定性控制等技术来实现钒铁矿协同开采。根据铁矿“中间厚、两端薄”、钒矿“中间薄、两端厚”的形态特征，将长走向的钒铁矿体分为东区、中区及西 区。工程空间上，双层矿体共用一套开拓、采准、运输等开采系统；开采时序上，在提高铁矿生产能力的同时保证了钒矿开采的时间灵活性；采矿方法上，东区及西区铁矿采用阶段矿房嗣后膏体微胶结充填法，中区 铁矿采用阶段矿房法转崩落法；此外，通过中区崩落顶板及上盘围岩，东、西区膏体充填方式保证了矿区开采时及开采后的区域稳定性。研究表明：所提出的协同开采方案使矿山铁矿设计开采储量增加了1 064.7万t ，膏体充填每年消耗干抛层、尾矿等矿山固废86万t以上，矿山安全及经济效益明显。     

Warm-white light performance of Dy3+, Eu3+: NaLa(WO4)2 phosphors excited with a 450-nm LED

Dy³⁺, Eu³⁺: NaLa(WO₄)₂ phosphors are successfully synthesized through the solid-state reaction technique. The phase-structure and morphology are measured via X-ray diffraction and energy dispersive spectrometry. The concentrations of Dy³⁺, Eu³⁺, La³⁺, and W⁶⁺ are measured via ICP. The absorption and excited spectra are presented, which indicate that a blue band ranging from 430 to 480 nm is suitable for excitation. Using a commercial blue LED with a wavelength of 450 nm as the excitation light source, emission spectra for samples with varying dopant concentration ratios of Dy³⁺ to Eu³⁺ are obtained, which show good tunable yellow and red emission. For the purpose of investigating white LED performance, CIE spectra and a white light photo are also presented. The results reveal that varying the dopant concentration ratio of Dy³⁺ to Eu³⁺ plays a key role in the warm-white performance. With increasing concentration of Eu³⁺, the correlated color temperature decreases from 4069 to 3172 K, which indicates good warm-white performance.     

Investigations on grinding process of woven ceramic matrix composite based on reinforced fiber orientations

Fiber orientations play the decisive role in grinding process of woven ceramic matrix composites, but the influence of woven fibers in grinding process is not clear. This paper studies the surface quality and grinding force by comparing different woven surfaces. Through a series of experiments in optimized sampling conditions, we analyze characteristics of the material surface topography height, wave distribution and surface support properties in details. And we find some outstanding characteristics of the surface microstructure. We also study the influence of grinding processing parameters on surface microstructure. The results show that machining surface which contains more parallel fibers is rougher and more keenness than gauss surface. Grinding wheel speed and depth of cut have great influence on surface topography and surface support properties. And it is discovered that grinding forces are also highly dependent on fiber orientations. The mechanism of the grinding phenomena is also analyzed in this paper according to knowledge of fracture mechanics and mechanical damage phenomenology. The research obtained will be an important technical support on improving the processing quality of woven ceramic matrix composites.     

Ion beam induced evolution of surface morphology and optical properties of SnO2–ZnO nanocomposite thin films

SnO₂–ZnO nanocomposite thin films, prepared by a simple carbothermal reduction based vapor deposition method, were irradiated with 8 MeV Si³⁺ ions for engineering the morphological and optical properties. The surface morphology of the nanocomposites was studied by atomic force microscopy (AFM), while the optical properties were investigated by photoluminescence spectroscopy (PL) and Raman spectroscopy. AFM studies on the irradiated samples revealed growth of nanoparticles at lower fluence and a significant change in surface morphology leading to the formation of nanosheets and their aggregates at higher fluences. A tentative mechanism underlying the observed ion induced evolution of surface morphology of SnO₂–ZnO nanocomposite is proposed. PL studies revealed strong enhancement in the UV emissions from the nanocomposite thin film at lower fluence, while a drastic decrease in the UV emissions along with a significant enhancement in the defect emissions has been observed at higher fluences.     

Iron-binding peptides from whey protein hydrolysates: Evaluation,isolation and sequencing by LC–MS/MS

Iron–peptide complexes have been considered a promising source of more bioavailable iron, with reduced side effects as compared to iron salts. Whey protein isolate (WPI) hydrolyzed by alcalase, pancreatin or flavourzyme was ultrafiltered (cut off 5 kDa) and their fractions – retentates and filtrates – were evaluated for iron-binding capacity. The Fe–hydrolysate complexation reaction resulted in a dramatic increase in iron solubility at pH 7.0, from 0% to almost 100%. This result was obtained regardless of the molecular mass profile or the enzyme used to obtain the samples. Fractions from hydrolysate obtained with pancreatin (HP) were chosen to continue the study. The complexes formed with both fractions from HP were stable under simulated gastric digestion (50.8–89.4%). To identify the peptides with iron-binding capacity, the HP fractions were isolated by IMAC-Fe^3 +, and the retentate showed higher relative concentrations of iron-binding peptides than the filtrate. Iron-binding peptide sequencing, accomplished by LC–MS/MS, showed Glu and/or Asp in all the sequences, and their carboxylic groups were amongst the main iron-binding sites. WPI hydrolysis with pancreatin yields peptides that can form iron complexes with the potential to increase iron bioavailability and reduce its pro-oxidant effect.     

Yolk–shell structured iron carbide/N-doped carbon composite as highly efficient and stable oxygen reduction reaction electrocatalyst

We report a simple route to synthesize iron carbide/carbon yolk–shell composite via a facile two-step process including polymerization of pyrrole using Fe₃O₄ as a sacrificial template to form a Fe₃O₄/polypyrrole composite, followed by annealing at high temperature in N₂ atmosphere. The yolk–shell composite, with iron carbide (Fe_2.5C) embedded in nitrogen-doped carbon layers, shows impressively high catalytic activity and stability for oxygen reduction reaction in alkaline solution. Both the pyridinic-N and graphic-N in the shell of Fe₃O₄–PPy-700, together with the Fe_2.5C confined in carbon layers are believed to be the active sites for the ORR.